ZrO2 dental material ZP101-8 8YSZ

for dental restorationspowder

1. The powder melting effect is good and the coating density is high; 2. The interface has few pores and high bonding strength; 3. The powder flow rate is 30s / 50g, the powder feeding is uniform, and the coating thickness is uniform; 4. The coating has good thermal shock resistance and does not peel off. Chemical Composition - ZrO2 (HfO2)/Y2O3=92/8 mol% Y2O3 Content - 7.0-7.5 wt% HfO2 Content - <5wt% Al2O3 Content - <0.02wt% SiO2 Content - <0.02wt% Fe2O3 Content - <0.02wt% TiO2 Content - <0.02wt% Other - <0.05wt% Morphology - Hollow sphere Apparent density - 2.0-3.0g/cm3 Powder velocity - 20-60s/50g Monoclinic ZrO2 - <3wt% Thermal Conductivity - 0.8-1.3W/mK Thermal Expansion - 10um/m/℃ Size Distribution - D10 20-30um D50 40-60um D90 70-90um Product Description: ZP103-8 8Y is a sintering powder of 8% yttria stabilized zirconia (YSZ). The product contains a small amount of monoclinic zirconia with different particle size distribution, bulk density and chemical properties. The purity of ZP103-8Y is high. The material after sintering and the spherical particle shape of particle size distribution jointly determine that the material has reliable fluidity and structural stability. ZP103-8Y sintered powder is especially suitable for TBCs which need to increase porosity.