Thermoplastic dental material PMMA Splint E

PMMACAD/CAMmilling

Product
BEGO PMMA Splint E — Milled thermoplastic occlusal splints.

• Very high wearing comfort thanks to thermoplastic flexibility
• Self-adjusting, extremely break-resistant material that adapts to tooth anatomy
• Low minimum thickness enabling minimally invasive splint designs
• Safe and reproducible production process using CAD/CAM milling
• Free from harmful plasticizers such as BPA (bisphenol A)

Indication

• Manufacture of milled occlusal splints from BEGO PMMA Splint E

Technical specifications
Chemical composition:
Poly(m)ethylacrylate and cross-linking copolymers of methacrylic acid — > 90%
1.2-cyclohexane dicarboxylic acid diisononyl ester — < 10%

Material data:
Flexural strength (23 °C) — > 20 MPa
Flexural strength (37 °C) — < 20 MPa
Density — Approx. 1.1 to 1.2 g/cm3
Color — Transparent

Characteristics / technical specifications

• Chemical composition: Poly(m)ethylacrylate and cross-linking copolymers of methacrylic acid (> 90%)
• Plasticizer content: 1.2-cyclohexane dicarboxylic acid diisononyl ester (< 10%)
• Flexural strength at 23 °C: > 20 MPa
• Flexural strength at 37 °C: < 20 MPa
• Density: Approx. 1.1 to 1.2 g/cm3
• Color: Transparent
• Thermoplastic flexibility for high wearing comfort
• Self-adjusting and highly break-resistant material
• Low minimum thickness enables minimally invasive splint designs
• Manufacturing: CAD/CAM milling ensures safe and reproducible production
• Free from BPA and similar harmful plasticizers