Gold-palladium alloy dental material BegoPal® 300

alloymetalfor ceramic veneering

Overview

• Metal-to-ceramic alloy for a wide range of dental restorations, from single crowns to suprastructures.
• Copper-free composition suitable for patients with metal sensitivities.
• Light-coloured oxide layer improves ceramic shade matching.
• Alloyed with gold and silver for favourable melting, flow and soldering behaviour.
• Biocompatible and corrosion-resistant for durable prosthetic frameworks.

Indications / Clinical use

• Porcelain-fused-to-metal (PFM) crowns and bridges
• Anterior and posterior restorations
• Multi-unit suprastructures and frameworks in dental laboratories

Key properties

• High palladium content for reliable mechanical properties
• Copper-free formula reduces allergy risk
• Predictable ceramic firing due to light oxide

Technical details (table)
Item name: BegoPal® 300
Product description: Palladium-based metal-to-ceramic alloy
Content/amount: 1 g
Composition: Pd 75,2 · In 6,3 · Ag 6,2 · Au 6,0 · Ga 6,0 · Re · Ru
Base metal: Palladium
Color code: 8
Preheat temp. from: 850 °C
Preheat temp. to: 850 °C
Casting temperature: 1390 °C
Solidus temp.: 1120 °C
Liquidus temp.: 1310 °C
Vickers hardness: 265 HV10
Yield strength: 485 MPa
Elongation at break: 34 %
Density g/cm³: 11,2 g/cm³
Elastic modulus: 122 GPa
Iso type ISO22674: 4
CTE: 13,5 10ˉ⁶ Kˉ¹

Specifications / Technical data

• Item name: BegoPal® 300
• Product description: Palladium-based metal-to-ceramic alloy
• Content/amount: 1 g
• Composition: Pd 75,2 · In 6,3 · Ag 6,2 · Au 6,0 · Ga 6,0 · Re · Ru
• Base metal: Palladium
• Color code: 8
• Preheat temperature: from 850 °C to 850 °C
• Casting temperature: 1390 °C
• Solidus temperature: 1120 °C
• Liquidus temperature: 1310 °C
• Vickers hardness: 265 HV10
• Yield strength: 485 MPa
• Elongation at break: 34 %
• Density: 11,2 g/cm³
• Elastic modulus: 122 GPa
• ISO type (ISO22674): 4
• CTE: 13,5 · 10ˉ⁶ Kˉ¹
• REF / SKU: 61105