Alloy dental material BegoPal® S

metalfor dental restorationsfor ceramic veneering

Overview

• Suitable for veneering with composites and conventional ceramics
• Copper-free — ideal for patients with copper sensitivity
• Light-coloured oxide for improved ceramic shade matching
• Biocompatible and corrosion-resistant, designed for dental laboratory workflows

Applications

• Metal-to-ceramic restorations: crowns, bridges and frameworks
• Laboratory use for metal-ceramic bonding and veneering
• Suitable for aesthetic anterior and posterior restorations

Technical details
Item name: BegoPal® S
Product description: Palladium-based metal-to-ceramic alloy
Content/amount: 1 g
Composition: Pd 57.5 · Ag 31.5 · Sn 9.0 · In 2.0 · Re · Ru
Base metal: Palladium
Color code: 8
Preheat temp. from: 850 °C
Preheat temp. to: 850 °C
Casting temperature: 1450 °C
Solidus temperature: 1210 °C
Liquidus temperature: 1270 °C
Vickers hardness: 245 HV10
Yield strength: 510 MPa
Elongation at break: 5 %
Density: 10.7 g/cm³
Elastic modulus: 120 GPa
ISO type (ISO22674): 4
CTE: 14.4·10⁻⁶ K⁻¹

Specifications

• Item name: BegoPal® S
• Product description: Palladium-based metal-to-ceramic alloy
• Content/amount: 1 g
• Composition: Pd 57.5 · Ag 31.5 · Sn 9.0 · In 2.0 · Re · Ru
• Base metal: Palladium
• Color code: 8
• Preheat temperature: 850 °C
• Casting temperature: 1450 °C
• Solidus temperature: 1210 °C
• Liquidus temperature: 1270 °C
• Vickers hardness: 245 HV10
• Yield strength: 510 MPa
• Elongation at break: 5 %
• Density: 10.7 g/cm³
• Elastic modulus: 120 GPa
• ISO type (ISO22674): 4
• CTE: 14.4·10⁻⁶ K⁻¹