Product Overview
Model Resin V3 is an SLA material formulated for fast, high-accuracy production of models used in dental and general-purpose applications. It delivers crisp margins and precise contacts for restorative workflows and supports high-volume and rush-case production in dental labs and prototyping environments.

Compatibility

• Compatible build platforms: Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L
• Compatible tanks: Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3
• Compatible printers: Form 3, Form 3L, Form 3B, Form 3BL, Form 2

Key Features

• Fast-printing formulation optimized for SLA production workflows
• High dimensional accuracy with crisp margins and reliable contact points
• Suitable for high-volume runs and rush cases
• Available in cartridge volumes compatible with Form 3 Series
• Beige, matte finish appropriate for dental models and general-purpose prototypes

Applications

• Restorative dental models (crown and bridge)
• Implant analog models
• Orthodontic and diagnostic models
• Miniatures, figurines and display models
• Solid models and removable die models

Material Properties (summary)
Post-cured test data—values depend on post-cure conditions and sample preparation. Typical post-cured values: Ultimate Tensile Strength 48 MPa; Tensile Modulus 2300 MPa; Flexural Modulus 2200 MPa; Elongation at Break 4.8%; Flexural Strength 85 MPa; Notched Izod ~23–24 J/m; Heat Deflection Temp. 75 °C (@0.45 MPa).

Post-processing

• Wash printed parts in isopropyl alcohol (≥99%) or another compatible solvent to remove uncured resin.
• Post-cure to complete polymerization, reduce surface tack and reach intended mechanical properties (follow recommended time/temperature).

Bulk and Packaging
Available in multiple cartridge volumes for the Form 3 Series (examples: 1 L and 5 L). Graduated bulk-order discounts may apply based on purchased volume.

Technical Specifications

• Print technology: SLA
• Category: General purpose (dental)
• Minimum layer thickness: 50 micron
• Color / finish: Beige, matte
• Applications: Dental restorative models, implant analogs, orthodontic and diagnostic models
• Tensile Modulus: 2300 MPa (2.3 GPa)
• Flexural Modulus: 2200 MPa (2.2 GPa)
• Ultimate Tensile Strength: 48 MPa
• Elongation at Break: 4.8 %
• Flexural Strength: 85 MPa
• Notched Izod: ~23 J/m
• Unnotched Izod: 324 J/m
• Heat Deflection Temp. @ 1.8 MPa: 56 °C
• Heat Deflection Temp. @ 0.45 MPa: 75 °C
• Thermal expansion: 76 μm/m/°C
• Typical post-cure workflow affecting properties: wash in ≥99% isopropyl alcohol and post-cure (e.g., 60 °C for recommended duration); properties vary with geometry, orientation and settings.